Alloy 310 is an austenitic stainless steel that combines excellent high temperature properties with good ductility and weldability. It is typically used for elevated temperature applications as its high chromium and nickel content provide solid corrosion resistance, excellent resistance to oxidation, and superior strength in temperatures up to 2100°F. Due to its high chromium and nickel content, it is superior to 304 or 309 stainless in most environments.

VALUE ADDED SERVICES:

· Need a special length?

o We can custom level 3/8″ thick x 72″ x 186″ from our plate line to reduce scrap

· Polish plate inventory available

o We supply #4, #6, and #8 mirror finish

o Special polishes available

· Plate processing

· Dynamic water jet cutting

· Plate shearing

· Saw cutting

· Plasma cutting and high quality plasma cutting

· Machine cut rings and discs

Penn Stainless Alloy 310S Plate and Processed Flat Bar provides superior resistance to corrosion and heat exposure, in even the most demanding environments.

CORROSION RESISTANCE:

· Provides excellent corrosion resistance

· High chromium content allows for good aqueous corrosion resistance

· Excellent resistance at normal temperatures and also has good resistance to oxidizing and carburizing atmospheres

HEAT RESISTANCE:

· Good resistance to oxidation in intermittent service in air at temperatures up to 1040°C and 1150°C in continuous service.

· Good resistance to thermal fatigue and cyclic heating.

· Widely used where sulphur dioxide gas is encountered at elevated temperatures.

· Continuous use in 425-860°C range not recommended due to carbide precipitation, if subsequent aqueous corrosion resistance is needed

· Generally used at temperatures starting from about 800 or 900°C – above the temperatures at which 304H and 321 are effective.

FABRICATION:

· Commonly used in the heat treatment and process industries due to high temperature and corrosive environments

· Often fabricated into complex structures

· Roller-forms, stamps and draws readily

· Because 310 work hardens, severe forming operations should be followed by an anneal

WELDABILITY:

· Austenitic stainless steel is generally considered to be weldable

· Generally considered to have weldability equivalent to 304 and 304L

· Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion