Dozens of grades to meet your needs, strict implementation of standards. Stainless steel coils with high quality and low price. Large inventory. Advanced equipment. Industry leading. Complete models. Stable quality.
904L is a high-alloy austenitic stainless steel with low carbon content. The grade is intended for use under severe corrosive conditions. It has been application proved over many years and was originally developed to resist corrosion in dilute sulfuric acid. It is standardized and approved for pressure vessel use in several countries. Structurally, 904L is fully austenitic and is less sensitive to precipitation ferrite and sigma phases than conventional austenitic grades with high molybdenum content. Characteristically, due to the combination of relatively high contents of chromium, nickel, molybdenum and copper 904L has good resistance to general corrosion, particularly in sulfuric and phosphoric conditions.
· Good resistance to pitting and crevice corrosion.
· Very good resistance to stress corrosion cracking.
· Good resistance to intergranular corrosion.
· Good formability and weldability.
· Maximum service temperatures of 450 deg.C. (824 deg.F).
Stainless Steel Coil/Sheet/Plate Information | |||||||||
| Surface Finish | Grade Series | Thickness(mm) | Width(mm) | |||||
Main Dimension | |||||||||
20-850 | 1000 | 1219 | 1240 | 1250 | 1500 | ||||
Hot Rolled | No.1 / 2E | 201/304/316L | 2.2-12.0 | √ | √ | √ | √ | √ | |
Cold Rolled | 2B | 201/304/316L | 0.25-3.0 | √ | √ | √ | √ | √ | √ |
410S/430 | 410S/430 | 0.25-3.0 | √ | √ | √ | √ | |||
No.4 /Hairline Mirror / Linen SB | 201/304/316L | 0.22-3.0 | √ | √ | √ | √ | √ | √ | |
410S/430 | 410S/430 | 0.25-3.0 | √ | √ | √ | √ | √ | ||
BA | 201/304 | 0.2--1.8 | √ | √ | √ | √ | √ | √ | |
410S/430 | 410S/430 | 0.25-3.0 | √ | √ | √ | ||||
2BA | 304/410S/430 | 0.25-2.0 | √ | √ | √ | √ | |||
If you need, we can customize the size according to your requirements |
Chemical composition and mechanical properties of stainless steel coils | |||||||||
Grade | Chemical Composition (%) | Mechanical Performance | |||||||
C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.03 | 3.5/5.5 | 16.0/18.0 | - | HB≤241,HRB≤100, HV≤240 |
304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.0/20.0 | - | HB≤187,HRB≤90,HV≤200 |
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.0/14.0 | 16.0/18.0 | 2.0/3.0 | HB≤187,HRB≤90,HV≤200 |
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.0/14.0 | 16.0/18.0 | 2.0/3.0 | HB≤187,HRB≤90,HV≤200 |
410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | - | HB≤183, HRB≤88 HV≤200 |
430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | - | 16.0/18.0 | - | HB≤183, HRB≤88 HV≤200 |
· Metal pickling in sulfuric acid
· Production and concentration of phosphoric acid
· Use in seawater, brackish water, condensers, heat exchangers and pipe work in general
· Paper and allied industries
· Gas washing
· Chemical and pharmaceutical industries